CERALOG Product Catalog

CERALOG ® Product catalog 2021 | 33 Properties (ISO 13356) Chemical structure (in %): ZrO 2 + HfO 2 + Y 2 O 3 ≥ 99.0 Y 2 O 3 4.5 < … ≤ 6.0 HfO 2 ≤ 5 Al 2 O 3 ≤ 0.5 other oxides ≤ 0.5 Mechanical properties: Transversal strength ≥ 800 MPa Microstructure Median grain size ≤ 0.4 µm Physical properties: Density ≥ 6 g/cm 3 Radioactivity ≤ 200 Bq/kg Properties (ASTM F136) Chemical structure (in %): Al 5.5–6.5 V 3.5–4.5 Fe ≤ 0.25 C ≤ 0.08 N ≤ 0.05 O ≤ 0.13 H ≤ 0.012 Ti Rest Mechanical properties: Tensile strength ≥ 860 MPa Elongation at break ≥ 10 % Zirconia – Y-TZP Titanium alloy Ti6AI4V ELI PEKK Properties Chemical structure (in %): Precious metal content (Au, Pt, Pd, Rh) 74.5% Au 61% Ag 16.5% Pt 13.5% Cu 9.0% Mechanical properties: Hardness HV5 > 250 Tensile strength (Rm) > 800 MPa 0.2% Elongation limit (Rp 0.2%) > 700 MPa Elongation at break > 6% Physical properties: Melting range 950–1050 °C Density 15.7 g/cm³ Modulus of elasticity 96 GPa Color Light Yellow Properties Mechanical properties: Tensile strength (MPa) 138 MPa Transversal strength (MPa) 193 MPa Compressive strength (MPa) 207 MPa Elongation at break > 30% Physical properties: Melting temperature 360 °C Density 1.3 g/cm³ Water absorption after 24h < 0.2 % Modulus of elasticity 4.5 GPa PEEK Properties Mechanical properties: Tensile strength (MPa) 100 MPa Transversal strength (MPa) 165 MPa Compressive strength (MPa) 135 MPa Elongation at break 40 % Physical properties: Melting temperature 340 °C Density 1.3 g/cm³ Water absorption after 24h 0.5 % Modulus of elasticity 4.1 GPa Holisticor Materials